Pull-Off Behavior of Hand-Cast, Thermoformed, Milled, and 3D-Printed Splints.

PURPOSE: To investigate the insertion/pull-out performance of splints produced by hand casting, thermoforming, milling, and 3D printing. MATERIALS AND METHODS: A total of 120 identical mandibular splints (n = 8 specimens per group) were manufactured with hand casting, thermoforming, milling, and 3D printing. The splints were stored in water at 37°C for 10 days and then placed onto cobalt-chromium arches and fixed on one side. Forces were applied to the other side (centric, perpendicular 50 N, 1 Hz) at two different positions (teeth 46 and 44/45) to pull out, and the test was then reset. The number of pull-out cycles until failure was recorded. The fracture behavior of the splints was investigated and characterized as fracture in the loading position, fracture at the fixation, or combined fracture. Splints were pulled off until fracture as a control (v = 1 mm/minute). Finite element analysis was used to verify the results. Statistical analyses were conducted with one-way ANOVA, post hoc Bonferroni, Pearson correlation, and Kaplan-Meier log-rank tests (α = .05). RESULTS: The mean pull-off cycles varied from 7,839 (V-Print) to 1,600,000 (Optimill) at the tooth 46 position (FDI numbering system) and from 9,064 (Splint Comfort) to 797,750 (Optimill) at the 44/45 position. Log-rank test showed significantly (P < .001) different pull-out cycles between the systems (chi-square: 61,792 to 122,377). The thickness of the splints varied between 1.6 ± 0.2 mm (Splint Comfort) and 2.3 ± 0.1 mm (V-Print). Thickness and number of cycles were correlated (Pearson: 0.164; P = .074). The pull-off forces of the control varied significantly (P ≤ .040), ranging from 13.0 N (Keysplint) to 82.2 N (Optimill) at the tooth 46 position and from 25.2 N (Keysplint) to 139.0 N (Optimill) at the 44/45 position. CONCLUSIONS: The milled and cast splints survived more pull-off cycles than the printed or thermoformed splints. The pullout performance showed differences among the tested splint systems and indicated the influence of the material properties and processing.

Finite Element Analysis of Occlusal Interferences in Dental Prosthetics Caused by Occlusal Adjustment.

PURPOSE: To investigate the influence of occlusal interference using finite element analysis (FEA). MATERIALS AND METHODS: The FEA model designed for this study centered on an all-ceramic, bilayered, fixed partial denture (FPD) retained on the maxillary first premolar and first molar, with the second premolar replaced by a pontic. The surrounding structures-such as the neighboring teeth, antagonists, and periodontium-were modeled. Four different loading cases were designed at occlusal interferences of 0, 8, 12, and 24 µm and were loaded by a simulated bite force of 300 N. Principal and von Mises stresses, as well as strain, were evaluated for all included structures. RESULTS: For interferences of 12 and 24 µm, failure-relevant tensile stresses in the veneering layer were observed at the occlusal surfaces. Stress found in the zirconia FPD did not reach fatigue or flexural strength for any test load. CONCLUSION: Peak tensile stress was observed in close proximity to occlusal contact points, increasing with increasing occlusal interference. The FEA results suggest that the majority of occlusal stress is absorbed by the deformation of the periodontal ligament. Framework failure caused by the simulated interferences was not expected. Surface defects may ultimately lead to failure due to fracture or chipping, especially in cases of weaker ceramics or veneering.

Aging and fracture resistance of screw-retained implant-supported molar crowns fabricated from lithium disilicate containing virgilite.

Purpose To investigate aging and fracture resistance of screw-retained implant-supported single crowns (iSCs) fabricated from lithium disilicate containing virgilite (VLD). Materials and Methods iSCs were fabricated from VLD (CEREC Tessera, Dentsply Sirona) and lithium disilicate (control; n=8, e.max CAD, Ivoclar) and bonded to a Ti-base abutment. VLD crowns were luted either with (VLDc, n=8) or without (VLDw, n=8) a coupling agent. iSCs were cleaned, sterilized, and screw-retained on implants. Fracture force was determined after thermal cycling and mechanical loading (TCML). Results All crowns survived TCML. No significant differences in mean fracture forces were identified between VLDc 1583 N, VLDw 1694 N, and control 1797 N (P=0.639 ANOVA, P=1.000 Bonferroni). Conclusion Screw-retained iSCs fabricated from VLD provide acceptable stability, which is independent on the usage of a coupling agent for bonding to Ti-base abutments and sterilization. Int J Prosthodont 2023. doi: 10.11607/ijp.8369.

Twenty-year follow-up of functional treatment with a bionator appliance (part 2): a retrospective cephalometric analysis of skeletal and dentoskeletal changes.

OBJECTIVES: To investigate skeletal and dentoskeletal changes 20 years after bionator treatment. MATERIALS AND METHODS: Analog lateral cephalograms of 18 subjects treated with a bionator appliance during growth were digitized with a transmitted light scanner. Inclusion criteria were: increased overjet (≥4 mm), skeletal Class II, available lateral cephalograms before (T0), after (T1), and 20 years after (T2) treatment with only a Bionator. To assess standard cephalometric parameters, the software ivoris analyze was used. Data were analyzed using Friedman's two-way analysis of variance by ranks followed by Dunn's post hoc tests (P ≤ .05). RESULTS: During therapy (T0-T1), ANB decreased significantly by 1.9° and remained unchanged long term. SNA slightly decreased (-0.6°) during treatment, SNB and SNPg increased (+1.4°, +1.7°). All three parameters showed a significant increase at T2 (+1.2°, +1.6°, +1.6°). Vertical measurements (ML-NL, ML-NSL, NL-NSL) remained almost unchanged during therapy. NL-NSL also was unchanged during the long-term interval; ML-NSL and ML-NL decreased significantly (-3.4°, -4.9°). During treatment, the maxillary incisors retroclined (OK1-NL: -1.6°, OK1-NA: -0.6°), the mandibular incisors proclined (UK1-ML: +3.5°, UK1-NB: +4.9°), neither significantly. Long term, there was a nonsignificant tendency toward proclination of upper (OK1-NL: +0.1°, OK1-NA: +0.7°) and retroclination of lower incisors (UK1-ML: -1.5°, UK1-NB: -5°). CONCLUSIONS: Changes of ANB after bionator treatment without additional fixed appliances remained stable after 20 years. The observed long-term changes are probably consequences of well-known physiological and age-related processes.

Survival dependence of 3D-printed temporary materials on the filler content.

AIM: The aim of the present study was the evaluation of the in vitro performance and fracture force of 3D-printed anterior implant-supported temporary partial dentures (TPDs) with different filler content. MATERIALS AND METHODS: Identical anterior resin-based TPDs (tooth sites 11 to 13; n = eight per material) were 3D printed from methacrylate resins with different filler content. A cartridge polymethyl methacrylate (PMMA) material was used as a reference. After temporary cementation, combined thermal cycling and mechanical loading (TCML) was performed on all the restorations to mimic clinical application. Behavior during TCML and fracture force was determined, and failures were analyzed. Data were statistically investigated (Kolmogorov-Smirnov test, one-way ANOVA; post hoc Bonferroni, Kaplan-Meier survival; α = 0.05). RESULTS: Failure during TCML varied between three failures and total failure during loading time. Mean survival time varied between 93 ± 206 x 103 cycles and 329 ± 84 x 103 cycles. Significantly different survival cycles between the individual materials could be determined (Mantel Cox log-rank test: chi-square: 21,861; degrees of freedom (df) = 4, P < 0.001). A correlation between filler level and survival cycles could be found (Pearson: 0.186, P = 0.065). Fracture values of the surviving TPDs varied between 499 and 835 N. Failures were characterized by fracture of the connector (n = 24) followed by fractures at the abutment (n = 10). CONCLUSIONS: TDPs showed different filler-dependent survival. Individual 3D-printed materials provided comparable or even better performance than a standard cartridge system and might be sufficient for temporary application of at least half a year.

Pull-off behavior of hand-cast, thermoformed, milled and 3D printed splints.

PURPOSE: To investigate the insertion/pull-out performance of splints produced by hand casting, thermoforming, milling, and 3D printing. MATERIALS AND METHODS: A total of 120 identical mandibular splints (n = 8 per group) were manufactured with hand casting, thermoforming, milling, and 3D printing. The splints were stored in water at 37°C for 10 days and then placed onto cobalt-chromium arches and fixed on one side. Forces were applied to the other side (centric, perpendicular 50 N, 1 Hz) at two different positions (teeth 46 and 44/45) to pull out, and the test was then reset. The number of pull-out cycles until failure was recorded. The fracture behavior of the splints was investigated and characterized as fracture in the loading position, fracture at the fixation, or combined fracture. Splints were pulled off until fracture as a control (v = 1 mm/minute). Finite element analysis was used to verify the results. Statistical analyses were conducted with one-way-ANOVA, post hoc Bonferroni, Pearson correlation, and Kaplan-Meier log-rank tests (α = .05). RESULTS: The mean pull-off cycles varied from 7,839 (V-Print) to 1,600,000 (Optimill) at the tooth 46 position and from 9,064 (Splint Flex) to 797,750 (Optimill) at the 44/45 position. Log-rank test showed significantly (P < .001) different pull-out cycles between the systems (χ2: 61,792 to 122,377). The thickness of the splints varied between 1.6 ± 0.2 mm (Splint Flex) and 2.3 ± 0.1 mm (V-Print Splint). Thickness and number of cycles were correlated (Pearson 0.164; P = .074). The pull-off forces of the control varied significantly (P ≤ .040), from 13.0 N (Keysplint) to 82.2 N (Optimill) at the tooth 46 position and from 25.2 N (Keysplint) to 139.0 N (Optimill) at the 44/45 position. CONCLUSION: The milled and cast splints survived more pull-off cycles than the printed or thermoformed splints. The pull-out performance showed differences among the tested splint systems and indicated the influence of the material properties and the processing.

Fracture Load and Fracture Patterns of Monolithic Three-Unit Anterior Fixed Dental Prostheses after In Vitro Artificial Aging-A Comparison between Color-Gradient and Strength-Gradient Multilayer Zirconia Materials with Varying Yttria Content.

(1) Background: Due to advantages such as avoidance of chipping, pulp-friendly tooth preparation and cost reduction, zirconia is increasingly being used monolithically without veneering. Nevertheless, to enable good aesthetics, various multilayer systems have been developed. The aim of this study was to investigate the impact of different zirconia multilayer strategies and yttria levels on fracture load, fracture pattern, stress distribution and surface roughness. (2) Methods: Monolithic three-unit anterior FDPs were made from three different color-gradient zirconia multilayer materials with different yttria levels corresponding to varying strength and degrees of translucency grades (Katana HTML, STML, UTML, Kuraray) and one strength-gradient zirconia multilayer material (Katana YML, Kuraray) and artificially aged in a chewing simulator (1.2 × 106 load cycles, 50 N, 2 × 3000 thermocycles, 5−55 °C). Analyses of fracture load, fracture pattern, fracture surfaces, stress distribution and roughness were performed after the fracture load test. Shapiro−Wilk, Kruskal−Wallis, Mann−Whitney U-tests and one-way ANOVA were used (p < 0.05). (3) Results: Fracture loads of the high strength color-gradient material HTML and the strength-gradient material YML were comparable after 5 years of aging (p = 0.645). Increasing yttria levels resulted in a decrease in fracture resistance of 42−57% (p < 0.05). Surface roughness of different zirconia generations is comparable after polishing and aging. (4) Conclusions: Color-gradient multilayer zirconia materials and new strength-gradient zirconia materials with similar yttria levels in the basal layers show comparable mechanical properties and are suitable for anterior FDPs.

In Vitro Mastication Simulation and Wear Test of Virgilite and Advanced Lithium Disilicate Ceramics.

PURPOSE: To compare wear behavior, durability during in vitro mastication simulation, and fracture force of an established and a novel lithium disilicate CAD/CAM material, as well as to examine the impact of cementation and reduced ceramic thickness on durability and fracture force. MATERIALS AND METHODS: Specimens (n = 8 per group) were prepared from lithium disilicate (LS2; IPS e.max, Ivoclar Vivadent) and advanced lithium disilicate (ALD; Cerec Tessera, Dentsply Sirona). Specimens were polished, and two-body wear test and thermocycling were performed (50 N, 120,000 cycles, 1.6 Hz, H2O dist., 5°C/55°C, 600 cycles). Maximum vertical loss, surface roughness, surface roughness depth, and antagonist wear were determined. Single crowns (n = 8 per group; thickness 1.5 mm/1.0 mm) were manufactured from LS2 and ALD and mounted on human molar teeth with adhesive resin (AB; CalibraCeram, Dentsply Sirona), glass-ionomer cement (GIC; Ketac Cem, 3M ESPE), and hybrid glass-ionomer cement (HGIC; Calibra Bio, Dentsply Sirona). Thermocycling and mechanical loading (2 × 3000 × 5°C/55°C, 2 minutes, H20 dist., 1.2 × 106 50 N) were performed. Fracture force was determined by a universal testing machine (1446, ZwickRoell), and one-way analysis and Bonferroni post hoc test (α = .05) were used for statistical analyses. RESULTS: Mean (ALD: 210 ± 42.4 µm; LS2: 264.3 ± 56.1 µm) and maximum (ALD: 391.1 ± 86.3 µm; LS2: 518.3 ± 113.2 µm) wear between groups were significantly different (P ≤ .047). Fracture force varied between 1,911.4 ± 468.4 N (ALD/AB 1 mm) and 2,995.3 ± 880.6 N (LS2/GIC), without significant differences (P ≥ .152). CONCLUSION: ALD showed better wear behavior than LS2, but provided similar fracture force. Cementation and reduction of ceramic thickness had only minor effects on fracture force.

Effects of storage and toothbrush simulation on color, gloss, and roughness of CAD/CAM, hand-cast, thermoforming, and 3D-printed splint materials.

OBJECTIVES: The aim was to investigate color, gloss, or roughness of splint materials after storage in liquids and toothbrush simulation. MATERIALS AND METHODS: A total of 58 × 8 (n = 10 per material and group) specimens were fabricated (hand-cast, thermoforming, CAD/CAM-milled, 3D-printed materials); stored in air, water, coffee, red wine, and cleaning tablets; and investigated after fabrication, 24 h, two-, and four-week storage or toothbrushing. Color values (L*, a*, b*; ISO 11664-4:2008; CM-3500d, Konica-Minolta), gloss (ISO 2813:2014), and roughness values were determined (3D laser-scanning-microscope, KJ 3D, Keyence) before and after simulation or storage. STATISTICS: Levene-test, one-way ANOVA, Bonferroni post hoc test, between-subjects effects, Pearson correlation (α = 0.05). RESULTS: Color, gloss, and roughness altered due to contact with staining solutions/toothbrush simulation. Highest impact on color, gloss, and roughness presented the material followed by storage time (ΔE material (η2 = 0.239/p < 0.001), storage time (η2 = 0.179/p < 0.001); gloss (η2 = 0.751/p < 0.001) (η2 = 0.401/p < 0.001); Ra/Rz (η2 ≥ 0.801/p < 0.001) (η2 ≥ 0.416/p < 0.001)). Correlations were found between Rz and Ra (Pearson 0.887/p ≤ 0.001) or Rz and ΔE (0.517/p ≤ 0.001) or Ra and ΔE (0.460/p ≤ 0.001). CONCLUSIONS: Storage and toothbrushing were accompanied by a change in color, gloss, and roughness. Almost all materials showed visible discoloration after 4 weeks of storage. Gloss values decreased as storage time increased. The initial roughness and polishability were better with harder materials. CLINICAL RELEVANCE: Milled and 3D printed splints show good color, gloss, and roughness resistance after 4-week storage or toothbrush application.

Multilayer zirconia: Influence of positioning within blank and sintering conditions on the in vitro performance of 3-unit fixed partial dentures.

STATEMENT OF PROBLEM: Multilayer zirconia blanks comprise material layers with different optical and mechanical properties. Whether positioning within the blank, as well as variation in the sintering procedure, will lead to restorations with different properties is unclear. PURPOSE: The purpose of this in vitro study was to test the influence of sintering procedures and positioning in a multilayer blank on the in vitro performance of 3-unit zirconia fixed partial dentures. MATERIAL AND METHODS: Human molars were embedded in acrylic resin and prepared for 3-unit fixed partial dentures. Anatomic contour prostheses were milled from zirconia blanks (ZirCAD Prime 16 mm) in 3 different positions: above (cusp-top at the top of the blank), central (center of the prosthesis in the center of the blank), and bottom (margins at the lower edge of the blank). Sintering time (2:26, 4:25, 9:50 hours:minutes) was varied for the central and bottom prostheses. All prostheses were glazed and adhesively bonded. Thermocycling and mechanical loading was performed at 2×3000×5 °C/55 °C in distilled water for 1.2×106 cycles at a 50-N load. Then, fracture force was determined with a universal testing device by using central loading, a Ø12-mm steel ball, a 1-mm tin foil, and a rate of 1 mm/min. Failure was defined as 10% force drop or acoustic signal (crack). Statistical analysis was performed with 1-way ANOVA and Bonferroni correction (α=.05). RESULTS: All fixed partial dentures survived thermocycling and mechanical loading. Fracture forces varied between 1002 ±446 N (above; 9:50 hours) and 1760 ±607 N (central; 9:50 hours). The 1-way ANOVA revealed no statistically significant differences (P=.059) among the groups. Individual significant differences (P=.048) were found between prostheses from positions above, 9:50 hours, and central, 9:50 hours. For normal and long sintering times, fracture forces were highest in the central position. CONCLUSIONS: The sintering process and positioning of restorations within a multilayer zirconia blank have little effect on the mechanical properties of the prostheses.

In vitro performance of CAD/CAM and conventional removable dentures.

AIM: Innovations in CAD/CAM technology and materials science offer new methodologies for removable prosthodontics. As clinical data are still rare, in vitro performance of both CAD/CAM and comparable conventional materials may help to estimate the clinical outcome. MATERIALS AND METHODS: Specimens (n = 8 per group) from teeth (CediTEC, SR VivodentCAD, Vitapan), base materials (V-Print dentbase, IvoBase CAD, Paladur), adhesives (CediTEC Primer/Adhesive, IvoBase CAD Bond), and a fully printed specimen (Try-In) were created. All specimens underwent thermal cycling and mechanical loading (TCML): 1,200,000 × 50 N; 2x3000 x 5°C/55°C; H2O. Surviving specimens were loaded to fracture. Statistical tests used were the Shapiro-Wilk test and the Kaplan-Meier survival, with the level of significance set to α = 0.05. RESULTS: Mean loading cycles until failure varied between 100 and 621,667 cycles. Up to five specimens per group failed during TCML. With one exception, all specimens of the entirely CAD/CAM-fabricated group survived TCML. The log-rank (Mantel-Cox) test showed significantly different (P = 0.000) loading cycles between the systems (chi-square test: 28,247; degree of freedom: 8). Failure of the dentures during TCML was characterized by failure of the denture base (2x), denture tooth (13x), mixed base/tooth (3x) or adhesive between base and tooth (1x). CONCLUSION: TCML and fracture testing showed different aspects of denture tooth restoration. The results indicated no correlation between fracture force, fracture pattern, and survival cycles. Denture teeth (milled, heat-pressed), bases (milled, printed, pressed), and primer should be matched up to optimize the performance of dentures.

Thermoanalytical Investigations on the Influence of Storage Time in Water of Resin-Based CAD/CAM Materials.

New resin-based composites and resin-infiltrated ceramics are used to fabricate computer-aided design (CAD) and computer-aided manufacturing (CAM)-based restorations, although little information is available on the long-term performance of these materials. The aim of this investigation was to determine the effects of storage time (24 h, 90 days, 180 days) on the thermophysical properties of resin-based CAD/CAM materials. Thermogravimetric Analysis (TGA), differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) were used in the study. TGA provided insight into the composition of the resin-based materials and the influence of internal plasticization and water sorption. Resin-based composites showed different decomposition, heat energy and mechanical behavior, which was influenced by storage time in water. Individual materials such as Grandio bloc showed lower influence of water storage while maintaining good mechanical properties.

Dynamic fatigue of 3D-printed splint materials.

OBJECTIVES: Printed splints may be an alternative treatment for functional disorders. In addition to the selection of materials, the influence of cleaning or polymerisation can affect the dynamic behaviour and fatigue limit of printed materials. MATERIAL AND METHODS: 96 discs (n = 6 per group, 16mmx2mm) were printed (P30+ DLP-printer, Straumann, CH; 100 µm layer) from splint materials (M1: Luxaprint OrthoPlus, DMG, G; M2: V-Print Splint, Voco, G). Specimens were either automatically cleaned (C1: Straumann P Wash, Straumann, CH) or manually cleaned (C2: Voco Pre-/Main-Clean protocol, Voco, G). Post polymerisation was performed with LED (P1: Cure, Straumann, CH) or Xenon light (P2: Otoflash N171, Ernst Hinrichs Dental, G). The flexural fatigue limit was determined under cyclic loading in terms of a staircase approach with a piston-on-3-ball-test according to ISO 6872 after 24 h or 60 days water storage (37 °C). Specimens were preloaded with 50N and dynamic force was applied for 105 loadings per step (f = 3Hz; steps 1: 50N-100N, 2: 50N-150N, 3: 50N-200N, 4: 50N-250N; F1000, Prematec, G; water at 37 °C). STATISTICS: Kaplan Maier Log Rank (Mantel-Cox) test, ANOVA, Pearson correlations, Levene-test (α = 0.05, SPSS 26.0, IBM, Armonk, NY, USA)). RESULTS: Mean survival cycles after 24 h of storage varied between 40388 (M1C2P2) and 195140 (M2C2P1) cycles and after 60 d decreased to 14022 (M1C2P2) and 173237 (M2C1P1). Kaplan Maier Log Rank test revealed significant differences between the material combinations. For M1 cleaning (Pearson: 0.346, p = 0.016) and for M2 polymerisation (Pearson: 0.616, p = 0.000) significantly influenced the number of loading cycles. Intermediate effects were found for material (p = 0.026), cleaning (p = 0.024) and polymerisation (p = 0.000) as well as the combination of material and polymerisation (p = 0.008). CONCLUSIONS: The results show that the number of possible loading cycles of additively manufactured splint specimens depends on the type of material, their cleaning and post-polymerisation. CLINICAL SIGNIFICANCE: Materials, cleaning and post-polymerisation of additive manufacturing processes should be matched to improve dynamic loading performance of splint materials.

Investigating the mechanical and optical properties of novel Urethandimethacrylate (UDMA) and Urethanmethacrylate (UMA) based rapid prototyping materials.

OBJECTIVE: This study is focused on testing experimental rapid prototyping materials for occlusal splints made from Urethandimethacrylate (UDMA) and Urethanmethacrylate (UMA). METHODS: Materials were mixed from UDMA and UMA in ratios of 1.0:0.0, 0.75:0.25, 0.5:0.5, 0.25:0.75 and 0.0:1.0. Specimens were printed using digital light processing (DLP). After post-processing, the specimens underwent testing on flexural strength, modulus of elasticity, hardness, wear behavior, surface roughness, gloss and color stability. All tests were performed after 24 h (baseline) and 10 days of water storage (aging). Splints underwent cyclic pull-off and insertion testing, which was alongside simulated using finite element analysis. RESULTS: The mechanical properties were significantly influenced by changes in the UDMA:UMA ratio. Statistical analysis revealed that increased amounts of UMA correlated with a decrease in flexural strength (92.0 to 30.7 MPa), modulus of elasticity (2.4 to 0.6 GPa), hardness (155.1 to 102.0 N/mm2) and wear resistance (-1394.9 to -1742.1 µm). Materials with higher amounts of UMA were also more likely to be influenced by water storage. Specimens with 75% and 100% UMA content were partly not analyzable due to soft consistency. Optical properties showed only minor influence from UMA content and aging. Differences in surface roughness (3.9 to 2.4 µm) and color stability were insignificant. Gloss was partly influenced by the UDMA:UMA ratio and water storage. Mean survival rates for cyclic pull-off and insertion testing ranged from 2537 to 23,857 cycles. A correlation between the amount of UMA and survival rates was observed. SIGNIFICANCE: The addition of up to 25% UMA showed promising results, complying with clinical standards and delivering acceptable results in the cyclic pull-off and insertion test. Further investigation on increments between 0 and 25% UMA could help to find an optimum.

Pilot in-vitro study on insertion/removal performance of hand-cast, milled and 3D printed splints.

OBJECTIVES: The aim of this in-vitro pilot study was to establish a splint testing method and compare insertion/removal performance of dental splints. MATERIALS AND METHODS: 56 identical lower jaw splints (n = 8 per group) were manufactured from 2x methacrylate (MA) hand-cast (reference material), deep-drawn Polyethyleneterephthalate, combined deep-draw MA hand-cast, 2x CAD/CAM-milled MA and 3D-printed MA systems. After 10 days water storage (37 °C), cyclic pull-off and insertion performance on a metal jaw was investigated. Statistics; Shapiro-Wilk-test, one-way-ANOVA; post-hoc-Bonferroni, Kaplan-Meier-survival, α = 0.05. RESULTS: Mean insertion/pull-off cycles varied significantly (p = 0.000) between 864 cycles (MA) and 202640 cycles (Deep Draw MA). Fracture of the splints was characterized by brittle individual fractures in the 31-34 region and most fractures in region 35 (44 of 56 splints). Finite element analysis confirmed the type and location of failure. CONCLUSIONS: Deep-draw, cast methacrylate and combined systems showed longer insertion/pull-off system cycles in comparison to printed or milled splints. Insertion/pull-off performance showed differences between the tested splint systems and indicates the influence of the processing. CLINICAL RELEVANCE: The presented in-vitro test allowed for estimating the clinical insertion/pull-off performance of dental splints.

Prognosis of multifactorial outcome in lumbar discectomy: a prospective longitudinal study investigating patients with disc prolapse.

OBJECTIVES: Although previous research has shown that certain medical data and psychosocial factors predict postoperative pain, it remains unclear whether they also contribute to a more distinct outcome measure that is based on classification of self-reported outcome criteria. To assess the prognostic power of somatic, psychologic, and social predictors when evident outcome criteria of surgical treatment are investigated, this study used a prospective longitudinal design examining preoperative factors associated with outcome six months after lumbar discectomy. METHODS: Forty-eight out of 58 consecutive patients were included (60% male, 40% female, mean age 47 years). Preoperative data comprised of Lasegue sign (straight leg raising test), pain duration, paresis and radicular distribution, depression, pain disability, pain coping strategies, and qualitative descriptions of pain. Additionally, sociodemographic and occupational characteristics were observed. Six months' postoperative classification of outcome included pain intensity, pain locations, functional capacity, return to work, and health-related quality of life. RESULTS: From a surgical point of view, lumbar discectomy was successfully carried out on all patients. But, when subjective criteria of outcome were investigated, 56% of patients benefited from lumbar discectomy, whereas 44% of patients had poor results. Lasegue sign, depression, and sensory pain descriptions proved to be significant predictors, whereas pain cognition and pain coping strategies had no significant influence on evident outcome classification. DISCUSSION: Classification of patients regarding their individual outcome profiles showed that patients responded differently to lumbar disc-surgery. High risk factors for poor outcome of surgery are Laseque-sign and depression.